7010 Aluminium Alloy offers exceptional strength and fatigue resistance, along with stress corrosion resistance, making it ideal for aerospace and mechanical engineering components subjected to high loads, though not recommended for elevated temperature applications.
Chalco has solidified partnerships with aerospace leaders such as Boeing, Collins Aerospace, and Airbus, supported by its robust capabilities. With AS9100, ISO, and other certifications, Chalco guarantees its products meet the rigorous standards of the aerospace industry.
- QQ-A-250/4, QQ-A-250/5,
- BS EN573, BS EN485
- AMS 4205, AMS 4035, AMS 4037, AMS 4027, AMS 4040, AMS 4041
- FMS 10101, BMS 7-305.
-
Quick Quote
Specification of Chalco 7010 aerospace aluminum plate
| Chalco 7010 aerospace aluminum plate specification | |
| Alloy | 7010 |
| Temper | T7451 T7651 O |
| Thickness | 6.35mm-203mm |
| Width | 500-2650mm |
| Length | 500-12000mm |
| Standard | AMS4083, AMS QQ-A-250/19, ASTM B209/B209M |
Chalco 7010 aerospace aluminum plate products
-
7010 hot rolled aluminum plate
High strength and formability, used in aircraft and spacecraft structural components.
-
7010 cold rolled aluminum plate
Enhanced surface finish and dimensional accuracy for tight-tolerance aerospace applications.
-
7010 aluminum sheet coil
Versatile, corrosion-resistant material for aerospace component manufacturing.
-
7010 T6 T651 aluminum plate
Heat-treated for high strength, ideal for aircraft structural parts and engine components.
-
7010 T7351 aluminum plate
High strength and machinability after artificial cooling, suitable for aerospace structural parts.
-
7010 T74 T76 aluminum plate
Tailored mechanical properties for critical aerospace structural elements.
-
7010 T7451 aluminum plate
Achieves high strength through artificial cooling, ideal for aircraft and spacecraft components.
-
7010 O aluminum plate
Annealed for high plasticity, used in simple aerospace components manufacturing.
Chemical composition of 7010 aerospace aluminum plate
| Chemical | Alloy 7010 |
| Zn | 5.2%-6.2% |
| Mg | 1.4%-2.1% |
| Cu | 0.1% |
| Mn | 0.1% |
| Cr | 0.04%-0.35% |
| V | 0.18%-0.28% |
| Ti | 0.04%-0.08% |
| Al | Remainder |
Mechanical properties of 7010 aluminum sheet plate
| Temper | Mpa Rm | Mpa Rp0.2 | Elongation A (%) | Hardness HBW Typical |
| T6 | 540 | 490 | 2 | 180 |
| T651 | 540 | 490 | 2 | 180 |
| T7351 | 450 | 360 | 5 |
Properties of Chalco 7010 aerospace aluminum sheet
Chalco Aluminum 7010 aerospace aluminum sheet is a high-strength, high-toughness aluminum alloy material whose composition mainly includes aluminum, zinc and magnesium. It is widely used in aerospace because of its excellent properties, including:
- High strength
- Good toughness
- Good corrosion resistance
- Excellent fatigue performance
- Good mechanical strength
- For low temperature applications
Application of Chalco 7010 aerospace aluminum sheet
- Aircraft structural parts
- Fuselage components
- Highly stressed parts
- Wing skins
Chalco other hot selling aluminum plate products
2024 aerospace aluminum plate
7075 aerospace aluminum plate
6061 aerospace aluminum plate
7050 aerospace aluminum plate
7475 aerospace aluminum plate
2219 aerospace aluminum plate
Instructions for maintenance of aerospace aluminum plate
- Before use, it must be ensured that the 7010 aluminum plate is in a dry and clean environment. Avoid long-term exposure of aluminum plates to harmful substances such as moisture, corrosive gases, dust, and pollutants.
- Aerospace aluminum plate can adopt conventional processing technology, such as cutting, forming and welding. However, due to its high strength and high toughness, higher-level processing equipment and tools may be required.
- Aerospace aluminum sheet can further improve its strength and mechanical properties through heat treatment. When performing heat treatments, proper temperature and time requirements must be followed to avoid negative effects on the material.
- Although most of the aerospace aluminum plate has high strength and high toughness, it still needs to be careful not to use it under overload or high stress, which may cause damage or damage to the material.
- To sum up, for the use of aerospace aluminum sheet, it is necessary to ensure that proper requirements and guidance are followed during its storage, processing, heat treatment and use to ensure its performance and service life.